EFFECTS OF STRAIN RATIO ON THERMAL-MECHANICAL CYCLIC STRESS-STRAIN RESPONSE AND FATIGUE LIFE IN DS SUPERALLOY DZ125
The effects of strain ratio on thermal-mechanical cyclic stress-strain response and fatigue life in DS superalloy DZ125 have been studied by performing tests at various strain ratio experiments, under strain-controlled and temperature cycling from 550to 1000 C. It is shown that thermal-mechanical cyclic stress-strain response behavior not only depend on magnitude of strain, and temperature-loading phase angle, but also strain ratio. Fatigue life at strain ratio Re=-0.3 is longer than that of strain ratio Rε=-1. 0, under in-phase thermal-mechanical loading. However, Fatigue life at strain ratio Rε=-0. 3 is shorter than that of strain ratio Rε=-1.0, under out-of-phase thermal-mechanical loading. The thermal-mechanical fatigue (TMF) damage model was discussed. Results of fractography show that fatigue, creep and oxidation damage always occur during TMF. The main damage mode depends on loading wave, strain ratio and magnitude of strain.
作 者： G.D.Zhang S.L.Liu Y.H.He R.Z.Chen 作者單位： Beijing Institute of Aeronautical Materials, Beijing 100095,China 刊 名： 金屬學報(英文版) ISTIC EI 英文刊名： ACTA METALLURGICA SINICA(ENGLISH LETTERS) 年，卷(期)： 2004 17(4) 分類號： 關鍵詞： thermal-mechanical fatigue in-phase out-of-phase【EFFECTS OF STRAIN RATIO ON THERMAL-M】相關文章：
Cause and Effects of Iron Deficiencies05-04
Effects of Formaldehyde Inhalation on Lung of Rats04-27
Environmental Effects on Microstructural Stability of SiC/SiC Composites04-26
Evaluation of dust activity and climate effects in North China04-26
Effects of sleep deprivation on gamma oscillation of waking human EEG04-26
EFFECTS OF ENSO ON THE RELATIONSHIP BETWEEN IOD AND SUMMER RAINFALL IN CHINA04-27
Effects of nutrients on Microcystis growth more easily forming bloom04-25
Analysis of sextupole effects on 13 function beating in the SSRF storage ring04-27
Effects of methamidophos and glyphosate on copper sorption-desorption behavior in soils04-25